Dataset: What causes the variation in superconducting properties of UTe2

https://doi.org/10.34863/7pbx-8g62
Authors: Caitlin S. Kengle ORCID logo ,0000-0002-1525-9483 , Noah Schnitzer ORCID logo 2,3, Mitchell M. Bordelon ORCID logo 1, Sean M. Thomas ORCID logo 1, Priscila F. S. Rosa1
Author affiliations:
1:Los Alamos National Laboratory, Los Alamos, NM 87545
2:Department of Materials Science and Engineering, Cornell University, Ithaca, NY, 14853, USA
3:Kavli Institute at Cornell for Nanoscale Science, Ithaca, NY, 14853, USA

Atomic resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) datasets and single crystal X-ray diffraction refinements on three single crystal samples of the unconventional superconductor UTe2 grown with different synthesis conditions and superconducting properties.

STEM Images
ItemTypeFile
STEM Images - Registered HAADF-STEM image of sample s1 on the [010] zone axisimageSTEM Images/20211004 1354 s1 010 rI.tif
STEM Images - STEM dataset of sample s1 on the [010] zone axisdataSTEM Images/20211004 1354 s1 010.emd
STEM Images - Registered HAADF-STEM image of sample s2 on the [010] zone axisimageSTEM Images/20211004 1710 s2 010 rI.tif
STEM Images - STEM dataset of sample s2 on the [010] zone axisdataSTEM Images/20211004 1710 s2 010.emd
STEM Images - Registered HAADF-STEM image of sample s1 on the [100] zone axisimageSTEM Images/20211103 1358 s1 100 rI.tif
STEM Images - STEM dataset of sample s1 on the [100] zone axisdataSTEM Images/20211103 1358 s1 100.emd
STEM Images - Registered HAADF-STEM image of sample s2 on the [100] zone axisimageSTEM Images/20211103 1530 s2 100 rI.tif
STEM Images - STEM dataset of sample s2 on the [100] zone axisdataSTEM Images/20211103 1530 s2 100.emd
X-ray refinements
ItemTypeFile
X-ray refinements - Sample s1 refined structure at 100 KdataX-ray refinements/UTe2_s1_100K.cif
X-ray refinements - Sample s1 reflections at 100 KdataX-ray refinements/UTe2_s1_100K.hkl
X-ray refinements - Sample s1 refined structure at 150 KdataX-ray refinements/UTe2_s1_150K.cif
X-ray refinements - Sample s1 reflections at 150 KdataX-ray refinements/UTe2_s1_150K.hkl
X-ray refinements - Sample s1 refined structure at 200 KdataX-ray refinements/UTe2_s1_200K.cif
X-ray refinements - Sample s1 reflections at 200 KdataX-ray refinements/UTe2_s1_200K.hkl
X-ray refinements - Sample s1 refined structure at 250 KdataX-ray refinements/UTe2_s1_250K.cif
X-ray refinements - Sample s1 reflections at 250 KdataX-ray refinements/UTe2_s1_250K.hkl
X-ray refinements - Sample s1 refined structure at 300 KdataX-ray refinements/UTe2_s1_300K.cif
X-ray refinements - Sample s1 reflections at 300 KdataX-ray refinements/UTe2_s1_300K.hkl
X-ray refinements - Sample s2 refined structure at 100 KdataX-ray refinements/UTe2_s2_100K.cif
X-ray refinements - Sample s2 reflections at 100 KdataX-ray refinements/UTe2_s2_100K.hkl
X-ray refinements - Sample s2 refined structure at 150 KdataX-ray refinements/UTe2_s2_150k.cif
X-ray refinements - Sample s2 reflections at 150 KdataX-ray refinements/UTe2_s2_150K.hkl
X-ray refinements - Sample s2 refined structure at 200 KdataX-ray refinements/UTe2_s2_200K.cif
X-ray refinements - Sample s2 reflections at 200 KdataX-ray refinements/UTe2_s2_200K.hkl
X-ray refinements - Sample s2 refined structure at 220 KdataX-ray refinements/UTe2_s2_220K.cif
X-ray refinements - Sample s2 reflections at 220 KdataX-ray refinements/UTe2_s2_220K.hkl
X-ray refinements - Sample s2 refined structure at 300 KdataX-ray refinements/UTe2_s2_300K.cif
X-ray refinements - Sample s2 reflections at 300 KdataX-ray refinements/UTe2_s2_300K.hkl
X-ray refinements - Sample s3 refined structure at 100 KdataX-ray refinements/UTe2_s3_100K.cif
X-ray refinements - Sample s3 reflections at 100 KdataX-ray refinements/UTe2_s3_100K.hkl
X-ray refinements - Sample s3 refined structure at 150 KdataX-ray refinements/UTe2_s3_150K.cif
X-ray refinements - Sample s3 reflections at 150 KdataX-ray refinements/UTe2_s3_150K.hkl
X-ray refinements - Sample s3 refined structure at 200 KdataX-ray refinements/UTe2_s3_200K.cif
X-ray refinements - Sample s3 reflections at 200 KdataX-ray refinements/UTe2_s3_200K.hkl
X-ray refinements - Sample s3 refined structure at 250 KdataX-ray refinements/UTe2_s3_250K.cif
X-ray refinements - Sample s3 reflections at 250 KdataX-ray refinements/UTe2_s3_250K.hkl
X-ray refinements - Sample s3 refined structure at 300 KdataX-ray refinements/UTe2_s3_300K.cif
X-ray refinements - Sample s3 reflections at 300 KdataX-ray refinements/UTe2_s3_300K.hkl